Define flash in mould making ?
Answers were Sorted based on User's Feedback
unwanted moltenplastic material which
form on component is known as flash
Is This Answer Correct ? | 2 Yes | 0 No |
Answer / karthikeyan..n
Injection pressure/injection rate too high
Barrel temperature too high
Insufficient clamping pressure
Mould sliding cores clearance too large Imprecise mould
alignment
Foreign material caused clearance on mould mating surface
Mould temperature too high Air venting design too large
Material over packed the mould cavity
Mould parting defects after age
Hopper temperature too high
Is This Answer Correct ? | 1 Yes | 0 No |
Answer / karthikeyan..n
Injection pressure/injection rate too high
Barrel temperature too high
Insufficient clamping pressure
Mould sliding cores clearance too large Imprecise mould
alignment
Foreign material caused clearance on mould mating surface
Mould temperature too high Air venting design too large
Material over packed the mould cavity
Mould parting defects after age
Hopper temperature too high
Is This Answer Correct ? | 1 Yes | 1 No |
Sir , i am a Mechanical Engg Student. Pls send me the JinDAL STEELS AND POWER LIMT.. RECRUITMENT DOMAIN AND APTITUDE BASED SAMPLE QUESTION Papers.. JINDAL IS MY DREAM JOB..PLEASE HELP ME AND GUIDE ME TO BE SUCCESS,I NEED THE SAMPLE QUESTIONS FOR URGENT. MY ID--sampathsurya@yahoo.com.
Dear friends, i am a student of mechanical final year in rajasthan. If you have any type (Technical,interview, aptitude) of question paper related to BIRLA CEMENT LTD. than plz send me these paper at vinodsainikumar4@gmail.com thanks
What would your previous supervisor say your strongest point is?
What is meant by counter flow heat exchanger?
Which rays are produced by cobalt-60 in industrial radiography ?
what is the difference between codes,standards, specification?
what is unit of mechanical work nand piower ?
5 Answers Hindustan Unilever Limited,
• Describe your management style
What is orthographic drawing?
What is cri pumps & mechanical sael
Explain QH curve of a Centrifugal Pump?. Will it ever touch X axis?. If it ever touch when? When will you go for Reciprocating pump?. why can't you use centrifugal pumps for pumping viscous fluids?. Why head of a centrifugal pump is independent of density of fluid?.
welding electrodes consumption per ton of structural steel fabrication