Why do the Gamma Prime and Gamma Double Prime phases play
such an important role in promoting strength in the
superalloys?






Why do the Gamma Prime and Gamma Double Prime phases play such an important role in promoting stre..

Answer / arun s. watwe

Gamma prime and gamma double prime phases are Ni3Al and
Ni3Nb in composition, respectively. These have strength
much higher than the superalloy matrix and ductility
comparable to that of the matrix. As such, these afford one
ways to have a wide range of amounts (10-70 % by volume)and
tehreby property ranges using relatively inexpensive
alloying additions. Just as important are their ability to
retain their strength upto high temperatures and to
precipitate in extremely fine sizes uniformly throughout
the matrix.

Is This Answer Correct ?    3 Yes 0 No

Post New Answer




More Metallurgy Interview Questions

How do 304 stainless steel and 316 stainless steel weld to each other? I am hoping my medical device prospect will be able to weld a component made in 316 ss via metal injection molding toa 304 ss tube.

0 Answers  


In grey iron sulpher was above 0.15% what react on metal?

0 Answers  


When using mercury to recover very, fine gold from ore, define what is the best way to separate the gold laden mercury from the ore?

0 Answers  


what are the causes of scaling in cast iron, after subjecting it to annealing process.

0 Answers  


what are the causes of delayed fracture in case hardened steels?

4 Answers  






Differentiate between stainless steel and alloy steel?

0 Answers  


What is the use of worm gears?

0 Answers   NIC,


How to melt the solidified copper accretions in copper scrap melting furnace?

0 Answers  


How much gold concentration should be in the organic phase (dbc) before reduction by oxalic acid solution? Is it effective on purity of gold in reduction step? Whatis the ratio of dbc to oxalic acid solution in this step?

0 Answers  


What is iron ferite? Where is it used?

0 Answers  


what is the different between ferrite percentage and ferrite number?

0 Answers  


Define what is the minimum temperature for stress relieving of astm a 519 gr.4130 material and please tell us where we can find the location.

0 Answers  






Categories
  • Civil Engineering Interview Questions Civil Engineering (5069)
  • Mechanical Engineering Interview Questions Mechanical Engineering (4441)
  • Electrical Engineering Interview Questions Electrical Engineering (16577)
  • Electronics Communications Interview Questions Electronics Communications (3915)
  • Chemical Engineering Interview Questions Chemical Engineering (1091)
  • Aeronautical Engineering Interview Questions Aeronautical Engineering (214)
  • Bio Engineering Interview Questions Bio Engineering (96)
  • Metallurgy Interview Questions Metallurgy (361)
  • Industrial Engineering Interview Questions Industrial Engineering (258)
  • Instrumentation Interview Questions Instrumentation (2986)
  • Automobile Engineering Interview Questions Automobile Engineering (332)
  • Mechatronics Engineering Interview Questions Mechatronics Engineering (97)
  • Marine Engineering Interview Questions Marine Engineering (122)
  • Power Plant Engineering Interview Questions Power Plant Engineering (170)
  • Textile Engineering Interview Questions Textile Engineering (575)
  • Production Engineering Interview Questions Production Engineering (0)
  • Satellite Systems Engineering Interview Questions Satellite Systems Engineering (106)
  • Engineering AllOther Interview Questions Engineering AllOther (1376)