Answer / karthikeyan.a

Carbon : 3.10 - 3.25%
Silicon : 1.75-1.95%
Manganese : 0.50 - 0.7%
Sulphur : 0.05 - 0.07%
Phosporous : 0.04 - 0.07%

Answer / m.ramamoorthy

cabon 3.2 to 3.5 %
si 1.9 to 2.2%
mn 0.5 to 0.7%
s 0.06%
p 0.09%

How much gold concentration should be in the organic phase (dbc) before reduction by oxalic acid solution?

0 Answers  

---

What is the atomic density of ceramics?

0 Answers  

---

what kind of cleaning substance or treatments keep or help prevent cast iron from rusting?

0 Answers  

---

I currently use 17-7 PH stainless which is hardened to condition CH after forming. raw matl is .1.75"X .12" X .008". Its main usage after hardening is silicon wafer retainer where it's contantly cycled up and down to putin and remove wafer after 40-60 sec process at 400C temp. At this high temperature this part seemed to deform after a a couple of hundred wafer which is what it was designed for in the first place. THere is a proposal to go to a different material to increase lifeline of this part. My question is..... can 321 SST be a plugin replacement. I know this has a higher temp rating but how about its forming characteristics, will it have spring properties, and wont become brittle after prolonged exposure to 400C.

0 Answers   Novellus,

---

What is the difference between DI pipes, Cast Iron pipes, LA Pipes, SW pipes, SWR Pipes, RCC hume pipe, RCC spun pipe ? What are their IS codes and applications ?

0 Answers  

---

---

Why cutting fluid is used in machining?

0 Answers   NIC,

---

Are the grain boundaries a continuation of regular lattice structure from one grain to another? Explain.

0 Answers  

---

Isn't power metallurgy an expensive processing route to employ?

2 Answers   JSW, TATA,

---

What is calibration of an instrument?

0 Answers   Essar,

---

Define what is the difference between stainless steel and alloy steel?

0 Answers  

---

Which material is used to made up of electrodes of resistance welding?

0 Answers   NIC,

---

What is a cryogenic fluid?

0 Answers   Essar,

---