what is the difference beteeen Annealing and stress
releaving
Answer Posted / arnab bakshi
Annealing is done to soften the material for Machining and
core refining. Where as Stress Releiving carried out to
remove stresses from Febrication Body, Casting Components
for Weather distortion, Heavy Maching stresses for avoiding
distortion in Hardning process without decreasing the
hardness of the material.
Annealing(full) is usually carried out at temperatures
above Ac3, whereas Stress relieving is generally a
subcritical process.
Is This Answer Correct ? | 2 Yes | 0 No |
Post New Answer View All Answers
The requirement for ASTM A217 Gr. WC9 castings for valves components like Body and Bonnet were Normalising at 920+/- 20 Deg. C and Tempring 780+/- 20 Deg. C The specification calls furnace shall be calibtated within +/-14 deg. C The Heat Chart shows minimum temperature for normalising 900 to 920 Deg. C, but maximum temperature 960-990 Deg. C Tempering 780+/-20 Deg. C is within limits and accepted. Casting having integral test bars, heat trated along with castings passed in chemical znalysis and mechanical properties. Since normalising maximum temperature is not meeting specification, where castings can be salvaged or renormalised and retempered to meet specification. Whether it will have affect on remechanical properties testing
what are metallurgical microscopes?
what are different grades of mild steel available for making machine structure (housing)
For what reason would an aluminum casting, when applied with a powder coated paint finish, cause a poor finish to the paintwork.
what should be the exact suction capacity for 3 to 5 mt capacity lead rotary furnace and length of duct line for proper suction for same
What are the characteristics of the thermodynamic stage of a metal?
What is the use of piezometer
Explain the concept of casting and forging?
How we describe strain aging based on dislocation theory?
Why we are doing post heating in alloy steel welding?
In grey iron sulpher was above 0.15% what react on metal?
What is the major difference between quenching and annealing?
The size of shaper is specified by ?
Define boring.
what is the hardness of ohns before heat treatment process and hardness of en series before heat treatment process