Answer Posted / anil kamat
Investment castings are similar to sand casting except that
intricate shapes which require to be done in a single piece
mould without ireggularities are done using this method. In
this the pattern is made using wax and then the the mould
is filled with sand around the wax pattern and the the
mould is baked untill the moisture is removed and the wax
evaporates and the cavity is formed . Then the molten metal
is poured into the cavity to get the desired shaped casting.
Is This Answer Correct ? | 2 Yes | 0 No |
Post New Answer View All Answers
What is the function of washer?
What happens to the microstructure during service exposure?
We make aluminum moulds by press casting, can you suggest any thing so that the moulds should shine after casting?
What is iron ferrite and what is it used for?
Explain vacuum induction melting?
Define rivets.
What are the chemical composition of cast iron grade 20
What is iron ferrite and where is it found?
What metal cord transfers electricity, and how can I tell?
What is the most ductile metal?
Define what is special about the properties of chromium molybdenum steels that make them ideal for pressure vessels?
What is the difference between DI pipes, Cast Iron pipes, LA Pipes, SW pipes, SWR Pipes, RCC hume pipe, RCC spun pipe ? What are their IS codes and applications ?
Does case harden steel properties detoriates over time? Especially for guns, parts like bolt carrier, the brand new parts has been kept for 10 year and properly oiled. I am worried about its surface hardness to take the blow during firing.
The requirement for ASTM A217 Gr. WC9 castings for valves components like Body and Bonnet were Normalising at 920+/- 20 Deg. C and Tempring 780+/- 20 Deg. C The specification calls furnace shall be calibtated within +/-14 deg. C The Heat Chart shows minimum temperature for normalising 900 to 920 Deg. C, but maximum temperature 960-990 Deg. C Tempering 780+/-20 Deg. C is within limits and accepted. Casting having integral test bars, heat trated along with castings passed in chemical znalysis and mechanical properties. Since normalising maximum temperature is not meeting specification, where castings can be salvaged or renormalised and retempered to meet specification. Whether it will have affect on remechanical properties testing
Aircraft gasturbine is made of ?